Premixed 20 to 100mm thick cementitious bonded screed.
Vetotop CS537 is a single component cementitious bonded floor screed composed of hydraulic binders, silica sand, selected aggregates, and special additives. It is supplied as a dry powder in pre-weighed bags ready to use on-site, once mixed it will form a screed-able trowellable mortar that is applied in thicknesses between 20 and 100 mm.
Vetotop CS537 comes in 50kg/bag with a yield of 21.7 - 27.8 liters.
An original sealed bag of Vetotop CS537 has a shelf life of 12 months provided it is stored clear of ground in a dry and shaded place below 35ºC.
An original sealed bag of Vetotop CS537 has a shelf life of 12 months provided it is stored clear of ground in a dry and shaded place below 35ºC.
The surface should be sound, clean, free from loose material, grease, laitance, dirt curing compound, etc.
Vetotop CS537 is a bonded screed that can be laid in thickness between 20 - 100 mm.
For more adhesion, an epoxy bonding agent can be used such as Vetobond EB430 or Vetobond EB431. Vetobond PB434 slurry can also be used.
To prepare the slurry primer mix 1 volume of Vetobond PB434 to 1 volume of clean water with 3 volumes of fresh cement and mix until a smooth consistency is achieved. Scrub the mixed slurry into the concrete surface, while the slurry is wet apply Vetotop CS537 in order to ensure good adhesion with the substrate.
Stated consumptions data are for general guidance. Actual consumption depends on the nature of the substrate, method of application and wastage.
For mixture preparation, pour into a container 4.5-5 liters of water for 50 Kg bag of Vetotop CS537.
Add the powder to the water and mix with a low speed electric drill fitted with a suitable paddle, until a uniform, lump free consistency mix is achieved. No further water should be added to the mix. Do not add water to the mix once it starts to set.
Pour the mixed product onto the surface and spread to the desired thickness using steel trowel or suitable tools. Cover the screed with a plastic sheet to avoid drying.
Cure the screed as per standard concrete curing practices. Do not subject the screed to vehicular traffic for 28 days till ensure full cure and systems ability to withstand designed traffic loads.
A concrete sealer is required for enhancing the screed durability and resistance to ingress of water, apply Vetoseal XW770 at a rate of 8 to 12 m2 per liter. Make sure that the sealer is uniformly applied and covering all screed surface.
Clean tools with water promptly before material hardens. Hardened material can be mechanically removed.
Vetotop CS537 is highly alkaline therefore avoid direct contact with eyes or skin. Vetobond PB434 is a latex emulsion. It is recommended to use protective gloves and goggles during application.
Any skin contact should be washed with plenty amount of water. In case of eye irritation, immediately wash with a copious amount of clean cold water. Seek medical advice.
Vetotop CS537 is non-flammable.
Saveto endeavors to ensure that any advice, recommendations, information it may give, is accurate and correct. It cannot accept any lia-
bility either directly or indirectly arising from the use of its products, because it has no direct or continuous control over where or how its products are applied, whether or not in accordance with any advice, specification, recommendation or information given by us.
Saveto has the right to change any of the specifications mentioned in the Technical data sheets upon its discretion without prior notifi- cation. Hard copies of TDSs are printed once or twice a year, while our technical data sheets are continuously being updated as per R&D improvements and new 3rd party testing; kindly refer to our website for the latest updated TDSs.
Polyurethane based heavy duty, waterproof and UV resistant car park decking system
Premixed 2 to 10 mm thick cementitious self leveling underlayment
Premixed 10 to 30 mm thick cementitious screed.
Premixed 30 to 100 mm thick cementitious screed.